12 years 2 months ago #1352 by Archived Forum Admin
Blow hole by the change of combustion ratio was created by Archived Forum Admin
Hi All,
We are facing surface quality problem on our wire rod where some fine flaw found after coiling. From the cross section analysis, the flaw is continue till the center. I supposed that it may cause by blow hole but I have no evidence to say that as I didn't found any blow hole when I cut my cast bar. Any one can help to explain the relationship between the change of combustion vs blow hole?

Regards
Berman

Please Log in to join the conversation.

  • Archived Forum Admin
  • Archived Forum Admin's Avatar Topic Author
  • Offline
  • Platnium Boarder
  • Platnium Boarder
More
12 years 2 months ago #1353 by Archived Forum Admin
Replied by Archived Forum Admin on topic Re: Blow hole by the change of combustion ratio
Hello again Berman,

I don't have the information you are looking for but perhaps the manufacturer of your continuous cast line will have that information. I suggest you go there first and see what you can find out because a specific answer here may take an extended period of time.

Moreover I could not find anything specific in the Wire Association abstract search of presented technical papers.

Regards
Peter J. Stewart-Hay
Principal
Stewart-Hay Associates
www.Stewart-Hay.com
519 641-3212

Please Log in to join the conversation.

Moderators: Erik A MacsPeter J Stewart-Hay
Time to create page: 0.064 seconds

Gallery

Contact us

The Wire Association Int.

71 Bradley Road, Suite 9

Madison, CT 06443-2662

P: (203) 453-2777