TOPIC: High speed winding

High speed winding 11 months 4 days ago #2707

  • Mr Nima Rahati
  • Mr Nima Rahati's Avatar
  • Junior Boarder
  • Posts: 25
  • Thank you received: 1
  • Karma: 0
Process : high speed winding
Problem : reduction in diameter of wire after winding in some areas (nonuniform diameter)

wire type : round copper wire
size : 0.30 and 0.32 mm
speed : 300 to 320 m/min
enamel type : polyester imide for base coat and self lubricant enamel for over coat
oven temperature :600 c
anneal temperature : 475 c
number of polyester passes:12 - 14 passes
number of overcoat passes : 1 pass (self lubricant)
external lubricant :solid lubricant
tension of wire : minimum
elongation : good
tangent delta : good
springback : good

Thanks very much for any information that can be provided.

Last Edit: 11 months 4 days ago by Peter J Stewart-Hay.
The administrator has disabled public write access.

Re: High speed winding 11 months 16 hours ago #2711

  • Richard Burke
  • Richard Burke's Avatar
  • Senior Boarder
  • Posts: 46
  • Thank you received: 4
  • Karma: 2
I think that either your tension is not consistent, your spooling is bad causing tension to vary or you have a torque control problem. Elongation is good but how good? I assume that you are using an inline drawing machine and if you are, the tensile strength should be greater than that of hard wire that is enameled. You should look at every place that the wire makes contact with the equipment. Check the sheaves to see that the bearing are free spinning.
Last Edit: 11 months 3 hours ago by Peter J Stewart-Hay.