make up natural cara make up make up tutorial make up korea make up minimalis make up artis make up mata belajar make up make up wardah alat make up makeup forever indonesia makeup artist jakarta tips make up barbie make up natural make up make up wajah make up pesta make up syahrini makeup mata makeup minimalis peralatan make up make up cantik make up mac make up kit jual make up make up sederhana perlengkapan make up gambar make up vidio make up cara makeup minimalis wardah make up make up pac make up glamour cara memakai makeup make up panggung harga make up make up modern make up alami make up dasar pixy make up make up muslimah make up oriflame make up jepang makeover cosmetic make up ultima make up sariayu grosir make up makeup fantasi makeup pesta tas makeup langkah make up make up pria make up malam alat makeup tahapan make up produk make up shading make up mak up make up kebaya make up jilbab make up inez make up simpel contoh make up cara ber makeup makeup wajah tanpa make up make up terbaru toko make up mac makeup indonesia make up soft urutan make up trik make up makeover makeup brand gusnaldi make up paket make up panduan make up jual makeup brush make up bagus alat2 make up make up gusnaldi aplikasi make up alat alat makeup dasar make up inez make up peralatan makeup make up wanita make up berjilbab make up tebal sejarah make up make up maybeline make up branded make up siang tata cara makeup reseller make up make up muslim make up maybelin warna make up tips make up artist rias make up make up mata make up artis belajar make up make up artist kursus make up kuas make up make up forever indonesia jual make up mac indonesia make up make up artist indonesia harga make up forever jual make up online make up pac make up forever jakarta make up oriflame jual make up forever make up online shop indonesia harga make up sekolah make up grosir make up harga make up maybelline jual make up murah make up terbaru mak up mac make up indonesia sofia make up make up kit murah mac makeup indonesia produk make up jual make up kit make up store indonesia make up forever academy jakarta toko make up online jual make up set jual make up mac make up beauty jual make up branded produk make up mac make up forever harga make up mac indonesia produk make up artis jual make up palette produk make up forever make up palette murah before after make up pengantin before after make up sendiri before n after hasil makeup contoh make up karakter contoh riasan pengantin before n after harga make up wisuda harga make up artist harga make up forever make up wisuda rias wisuda di jogja Daftar harga make up forever daftar harga make up mac daftar harga kosmetik make up forever makeup wisuda harga makeup wisuda kursus make up di yogyakarta kursus make up di jogja kursus make up jogja kursus make up yogyakarta kursus kecantikan di yogyakarta kursus kecantikan di jogja kursus make up artist di jogja kursus rias pengantin di jogja kursus rias di yogyakarta kursus tata rias di yogyakarta rias pengantin muslim jogja jasa kreasi jilbab wisuda yogyakarta jasa rias make up wisuda murah bagus bisa dpanggil tempat make uf di jigja yang bagus rias wisuda murah dan berkualitas yogyakarta pakar kreasi jilbab di jogja make uper natural yogya make up wisuda hijab area jogja make up dan kreasi jilbab yang bagus di jogja jasa make up natural untuk wisuda jogja makeup jogja make up jogja makeup yogyakarta make up yogyakarta makeup wisuda jogja make up wisuda jogja make up wisuda yogyakarta makeup wisuda yogyakarta
Search - People/Events
Search - Content
Search - Industry
Search - Forums
Search - Newsfeeds



jobcenterbanner

FacebookLinkedinPinterestYoutube
Welcome, Guest
Username: Password: Remember me
If you have a question regarding coaxial, telephone, and building wire, power cable, insulation, extrusion, bunching, stranding, braiding, etc. post it here.

TOPIC: Insulation of enameled copper wire

Insulation of enameled copper wire 2 years 7 months ago #751

We start to produce enameled copper wire and noticed that the insulation falls down from 5000 V at the moment of production to 3000 V after a week than to 1000 V after a few weeks. Do you think that the source of the problem is the annealing oven or the varnish oven. Thank you for your help.
The administrator has disabled public write access.

Re: Insulation of enameled copper wire 2 years 7 months ago #752

The answer to your question is neither. The annealer or oven only provide heat to ore-anneal the copper or to drive the solvents out of the liquid enamel or to dry it. The effect is short term or momentary at best unless you are over or under curing a product. If the product is good when it left the oven there is nothing that the oven can do to effect the wire once it is no longer in the oven.

I think your answer may be in your material. Is it a thermoplastic? The difference between thermoplastics and thermosetting plastics is that thermoplastics become soft, remoldable and weldable when heat is added. Thermosetting plastics however, when heated, will chemically decompose, so they can not be welded or remolded. On the other hand, once a thermoset is cured it tends to be stronger than a thermoplastic.

It is probably continuing to cure/downgrade even when sitting on the shelf.

This is not necessarily a problem if you are encapsulating it or putting it in an oil filled transformer. It is a big problem if you are trying to use it for motor windings and coil windings that are not totally encapsulated.

richard
Last Edit: 1 year 6 months ago by Peter J Stewart-Hay.
The administrator has disabled public write access.

Re: Insulation of enameled copper wire 2 years 7 months ago #753

Dear Richard,
Thank you very much for your information and help. We would like to inform you that we use a copper ETP grade A and polyester-imide enamels thermal class 200. We have noticed that the breakdown voltage remains unchanged for 0.75 mm and falls down after weeks for higher diameters (such 1.50 mm).

Best regards
Last Edit: 2 years 4 months ago by Archived Forum Admin.
The administrator has disabled public write access.

Re: Insulation of enameled copper wire 2 years 7 months ago #754

The type of copper used should not make a difference. I have never heard of this happening with this type enamel.
One thought that occurred is that this type enamel especially the overcoat is hydroscopic meaning that it picks up moisture from air. If you have a high ambient air humidity and a large open supply tank with slow turn over of the enamel, then if too much moisture is adsorbed, this may be the cause of the problem. Might be a stretch thought but if you can put a lid on your tank or reduce the volume, perhaps it would help.

rb
The administrator has disabled public write access.

Re: Insulation of enameled copper wire 2 years 7 months ago #755

Wire,
What you are experiencing with the polyester-imide sounds like a cure issue. 200c polyester-imide has a high glass transistion temperature along with a high curing temperature to achieve cross linking of the polymer. There are two tests that you can perform to test for cure. Firstly, you can check the tangent delta ( DF vs temperature ). This test should show two transitions. One at 200c and the other greater than 220c. The second test is old school. Place the coated wire in alcohol for approximately 2 hrs and then bend the wire. If it cracks ( the coating ) when you bend it, it is not cured properly. Increase temperature and reduce coating speeds. One last thing, you mentioned that one size does it and the other does not. For a starting point on production speed try this formula ( V/D ). Velocity times Diameter and then proprtion the other size.
The administrator has disabled public write access.

Re: Insulation of enameled copper wire 2 years 7 months ago #756

Dear tech1,
Thank you very much for your information. Our oven lenght is 9 m and its temperature is 550°c. We produce 0.75 mm with speed 70m/min. What should be the speed for producing 1.50 mm using the formula V/D.
Best regards,
Wire
The administrator has disabled public write access.