make up natural cara make up make up tutorial make up korea make up minimalis make up artis make up mata belajar make up make up wardah alat make up makeup forever indonesia makeup artist jakarta tips make up barbie make up natural make up make up wajah make up pesta make up syahrini makeup mata makeup minimalis peralatan make up make up cantik make up mac make up kit jual make up make up sederhana perlengkapan make up gambar make up vidio make up cara makeup minimalis wardah make up make up pac make up glamour cara memakai makeup make up panggung harga make up make up modern make up alami make up dasar pixy make up make up muslimah make up oriflame make up jepang makeover cosmetic make up ultima make up sariayu grosir make up makeup fantasi makeup pesta tas makeup langkah make up make up pria make up malam alat makeup tahapan make up produk make up shading make up mak up make up kebaya make up jilbab make up inez make up simpel contoh make up cara ber makeup makeup wajah tanpa make up make up terbaru toko make up mac makeup indonesia make up soft urutan make up trik make up makeover makeup brand gusnaldi make up paket make up panduan make up jual makeup brush make up bagus alat2 make up make up gusnaldi aplikasi make up alat alat makeup dasar make up inez make up peralatan makeup make up wanita make up berjilbab make up tebal sejarah make up make up maybeline make up branded make up siang tata cara makeup reseller make up make up muslim make up maybelin warna make up tips make up artist rias make up make up mata make up artis belajar make up make up artist kursus make up kuas make up make up forever indonesia jual make up mac indonesia make up make up artist indonesia harga make up forever jual make up online make up pac make up forever jakarta make up oriflame jual make up forever make up online shop indonesia harga make up sekolah make up grosir make up harga make up maybelline jual make up murah make up terbaru mak up mac make up indonesia sofia make up make up kit murah mac makeup indonesia produk make up jual make up kit make up store indonesia make up forever academy jakarta toko make up online jual make up set jual make up mac make up beauty jual make up branded produk make up mac make up forever harga make up mac indonesia produk make up artis jual make up palette produk make up forever make up palette murah before after make up pengantin before after make up sendiri before n after hasil makeup contoh make up karakter contoh riasan pengantin before n after harga make up wisuda harga make up artist harga make up forever make up wisuda rias wisuda di jogja Daftar harga make up forever daftar harga make up mac daftar harga kosmetik make up forever makeup wisuda harga makeup wisuda kursus make up di yogyakarta kursus make up di jogja kursus make up jogja kursus make up yogyakarta kursus kecantikan di yogyakarta kursus kecantikan di jogja kursus make up artist di jogja kursus rias pengantin di jogja kursus rias di yogyakarta kursus tata rias di yogyakarta rias pengantin muslim jogja jasa kreasi jilbab wisuda yogyakarta jasa rias make up wisuda murah bagus bisa dpanggil tempat make uf di jigja yang bagus rias wisuda murah dan berkualitas yogyakarta pakar kreasi jilbab di jogja make uper natural yogya make up wisuda hijab area jogja make up dan kreasi jilbab yang bagus di jogja jasa make up natural untuk wisuda jogja makeup jogja make up jogja makeup yogyakarta make up yogyakarta makeup wisuda jogja make up wisuda jogja make up wisuda yogyakarta makeup wisuda yogyakarta
Search - Content
Search - People/Events
Search - Forums
Search - Newsfeeds



jobcenterbanner

FacebookLinkedinPinterestYoutube
Welcome, Guest
Username: Password: Remember me
Nonferrous topics such as copper and aluminum, annealing, etc. go here.

TOPIC: Copper Wire Annealing

Copper Wire Annealing 2 years 6 months ago #1534

Can #2 AWG copper wire be in-line annealed as it pays off from the draw line? If yes, please explain how this can be accomplished with standard equipment or if no, what are the alternatives.

Thanks in advance for your help,
Raoul
The administrator has disabled public write access.

Re: Copper Wire Annealing 2 years 6 months ago #1535

Hello Raoul,

Wow, that's one big copper conductor for in-line electric annealing! (0.257626 inches or 6.543707 mm) I am personally not aware of any company that manufacturers electric in-line electric annealers for copper wire that large. However, sometimes Mr. H.G. Queins ( www.queins.com/de/welcome/ ) ( This email address is being protected from spambots. You need JavaScript enabled to view it. ) has knowledge of such esoteric machinery.

If there are no in-line electric annealers, then the next logical step would be to review copper batch annealers such as those manufactured by Ebner Industrieofenbau Gesellschaft m.b.H in Austria ( www.ebnerhicon.at/ ). Make sure however you have a detailed discussion with them about hydrogen embrittlement and delayed hydrogen embrittlement so that you are comfortable with that subject. You must not end up with hydrogen embrittlement. See thread www.wirenet.org/forum/viewmessages.cfm?forum=12&topic=493

Kindest regards,
Peter J. Stewart-Hay
Principal
Stewart-Hay Associates
www.Stewart-Hay.com
The administrator has disabled public write access.

Re: Copper Wire Annealing 2 years 6 months ago #1536

Hello Raoul,
Here is one source for inline annealing AWG 2.
Niehoff provide several annealers (electrical or inductive) also for bigger diameters (rod break down)
One annealer for the AWG 2 could be the R 800.
Please contact us.

Best Regards
Frank Knobloch
This email address is being protected from spambots. You need JavaScript enabled to view it.
The administrator has disabled public write access.

Re: Copper Wire Annealing 2 years 6 months ago #1537

Greetings from Toronto,
Peter is forgetting the possible use of Plasma Annealing systems ( www.plasmait.com ) for which neither speed nor diameter present a problem.

However, if the wire can be annealed with a "simple" resistance annealer, as Frank correctly indicates, it will be the most practical solution.

Best Regards,
Willy Hauer
Howar Equipment Inc.
www.howarequipment.com
The administrator has disabled public write access.

Re: Copper Wire Annealing 2 years 6 months ago #1538

Willy, we did not forget you. We reviewed the Plasmait web site and the maximum diameter we could find in the annealer section was 5 mm. which is a little smaller than 4 AWG.

Frank, we did not forget you either. We went to your web site in Germany. The largest in-line electric annealer you show is the R 560 and the largest single copper wire is 5.60 mm. or about 3.5 AWG.

We also checked the SAMP and Lesmo web sites and found no larger in-line electric annealers.

We believed those to be the four best options.

Gentlemen, if we cannot find it on your web site, we do not read minds.

None the less we are very pleased that you responded.

Best regards to the both of you,
Peter J. Stewart-Hay
Principal
Stewart-Hay Associates
www.Stewart-Hay.com

PS. Frank We noticed that for some reason, you are adding two copies to your original posting each time. If you are having some sort of problem, please contact me at ( This email address is being protected from spambots. You need JavaScript enabled to view it. ) and we will see if we can correct it.

Willy. Please always leave a space before and after a web site addresses or an E-mail addresses. Then the links should work properly for you. If you still have problems and you know how to write HTML, the modified HTML pre-written commands here are very easy to use.
The administrator has disabled public write access.

Re: Copper Wire Annealing 2 years 6 months ago #1539

I read the original problem with interest and thought that a long time ago Syncro had an annealer that would do this size. I also thought about plasma annealer but the only one I have seen for copper wire was also on an enamelling system and while the line speed was fairly high (not compared to same size wire drawing) the wire was small. One problem I could perhaps see is that the wire on the enamelling system was fairly clean entering the annealer.. not sure about 2 awg being similarly clean.

rb
The administrator has disabled public write access.