Air Patenting

  • Archived Forum Admin
  • Archived Forum Admin's Avatar Topic Author
  • Offline
  • Platnium Boarder
  • Platnium Boarder
More
12 years 2 months ago #870 by Archived Forum Admin
Air Patenting was created by Archived Forum Admin
Dear All,

We have an air patenting furnace 13 meters long with 3 burners to control the temperature and air fans from 2 sides, but sometimes patenting wire is cracked.

What is the suitable air pressure to get fine pearlite?

Thank you for your kind attentions,

Please Log in to join the conversation.

  • Archived Forum Admin
  • Archived Forum Admin's Avatar Topic Author
  • Offline
  • Platnium Boarder
  • Platnium Boarder
More
12 years 2 months ago #871 by Archived Forum Admin
Replied by Archived Forum Admin on topic Re: Air Patenting
To obtain fine perlite ( on high carbon wires), the wire should heat uniformily up to fully transformation temperature where it is fully austenized (+,-) 800 oC then sudenlly in few seconds the material should decrease temperature ( +,-)500oc. . The conditions for different carbon contents can be obtain in the TTT curves ( Temperatur, Time ,Transformatio). WAI has several presentations on the subject can be seen on his web page

Eduardo Anaya
Senior Consultant
INDEPA S.C.
Mexico City
Tel(011-52)555-407-7451
This email address is being protected from spambots. You need JavaScript enabled to view it.

Please Log in to join the conversation.

Moderators: Peter J Stewart-HayEduardo AnayaPeter M Power